Synthesis of a novel superabsorbent with slow-release urea fertilizer using modified cellulose as a grafting agent and flexible copolymer.

In this work, a number of glucose unites in polymeric structure of cellulose was converted to 2,4-dihydroxy-3-(1-hydroxy-2-oxoethoxy)butanal (cellulose containing di aldehyde units (CCDAUs)) by oxidation with sodium periodate, followed by condensation with acetone to produce 5,7-dihydroxy-6-((1-hydroxy-4-oxopent-2-en-1-yl)oxy)hept-3-en-2-one unites (cellulose containing di ene units (CCDEUs)). This modified cellulose was characterized by different methods and applied as a copolymer and grafting agent to synthesize an eco-friendly (CCDEUs-g-poly(AA)/urea) superabsorbent with slow-release urea fertilizer. The created double bonds in C2 and C3 positions of ß-d-glucose units increased the linkage between cellulose and acrylic acid, leading to the formation of a strong network for slow-release urea fertilizer. Also, this modification created an expanded network for storage a high amount of water by increasing the cellulose flexibility. The reaction conditions for modification and synthesis of the superabsorbent, the oxidation degree value of glucose units, kinetics models, the effect of different saline solutions, various pH and reswelling time on the water absorbency, water retention capacity, reusability, biodegradability, and slow-release property were investigated. Also, the effect of synthesized CCDEUs-g-poly(AA)/urea on plant growth was tested and excellent results were obtained.

PZT/PZT and PZT/BiT Composite Piezo-Sensors in Aerospace SHM Applications: Photochemical Metal Organic + Infiltration Deposition and Characterization.

The composition of fine-ground lead zirconate-titanate powder Pb(Zr0.52Ti0.48)O3, suspended in PZT and bismuth titanate (BiT) solutions, is deposited on the curved surface of IN718 and IN738 nickel-based supper alloy substrates up to 100 µm thickness. Photochemical metal organic and infiltration techniques are implemented to produce smooth, semi-dense, and crack-free random orientated thick piezoelectric films as piezo-sensors, free of any dopants or thickening polymers. Every single layer of the deposited films is heated at 200 °C with 10 wt.% excess PbO, irradiated by ultraviolet lamp (365 nm, 6 watt) for 10 min, pyrolyzed at 400 °C, and subsequently annealed at 700 °C for one hour. This process is repeated successively until reaching the desired thickness. Au and Pt thin films are deposited as the bottom and top electrodes using evaporation and sputtering methods, respectively. PZT/PZT and PZT/BiT composite films are then characterized and compared to similar PZT and BiT thick films deposited on the similar substrates. The effect of the composition and deposition process is also investigated on the crystalline phase development and microstructure morphology as well as the dielectric, ferroelectric, and piezoelectric properties of piezo-films. The maximum remnant polarization of Pr = 22.37 ± 0.01, 30.01 ± 0.01 µC/cm², the permittivity of εr = 298 ± 3, 566 ± 5, and piezoelectric charge coefficient of d33 = 126, 148 m/V were measured versus the minimum coercive field of Ec = 50, 20 kV/cm for the PZT/PZT and PZT/BiT thick films, respectively. The thick film piezo-sensors are developed to be potentially used at frequency bandwidth of 1⁻5 MHz for rotary structural health monitoring and also in other industrial or medical applications as a transceiver.